To discuss the problem of fatigue and fracture of cemented carbides, we must first understand these two concepts, namely what is fatigue and what is fatigue fracture.

Fatigue: The change in the properties of metal materials under repeated stress or strain is called fatigue.

Fatigue fracture: When a material is subjected to alternating cyclic stress or strain, it causes continuous development of local structural changes and internal defects, resulting in a decrease in mechanical properties of the material, ultimately leading to complete fracture of the product or material. This process is called fatigue fracture, and can also be referred to as metal fatigue. The stress causing fatigue fracture is generally very low, and the occurrence of fatigue fracture often has characteristics of suddenness, high localization, and sensitivity to various defects.

fatigue  carbide

Classification of fatigue fracture

High-cycle fatigue and low-cycle fatigue

If the stress level acting on the part or component is low, and the number of cycles of failure is greater than 100,000, it is called high-cycle fatigue. Products such as springs, drive shafts, and fasteners are generally characterized by high-cycle fatigue.

The stress level acting on the component parts is high, and the number of cycles of damage is low, generally less than 10,000 cycles of fatigue, which is called low-cycle fatigue. For example, the fatigue damage of pressure vessels and turbine parts belongs to low-cycle fatigue.

Stress and strain analysis

Strain fatigue – high stress, low cycle number, called low cycle fatigue;

Stress fatigue – low stress, high cycle number, known as high-cycle fatigue.

Composite fatigue, but in practice, it is often difficult to distinguish between stress and strain types, and in general, both types are present, which is called composite fatigue.

Classification by load type

Bending fatigue, torsional fatigue, tension-compression fatigue, contact fatigue, vibration fatigue, and fretting fatigue.

How does the fatigue fracture of cemented carbide material occur? 2

Characteristics of fatigue fracture

Macro: crack source → propagation zone → instantaneous fracture zone.

Crack source: The presence of grooves, defects, or areas of stress concentration on the surface is a prerequisite for the generation of crack sources.

Fatigue propagation zone: The section is relatively flat, with fatigue propagation perpendicular to the stress direction, resulting in a clear fatigue arc, also known as a beach or shell line.

Transient fracture zone: It is the area where fatigue cracks rapidly expand to instantaneous fracture. The fracture surface has traces of metal slip, and some products have radioactive stripes and shear lip zones in the transient fracture zone.

Microscopic: The typical characteristic of fatigue fracture is the appearance of fatigue striations.

Some microscopic samples also exhibit cleavage and quasi-cleavage phenomena (crystallographic terms for small planes that appear in microscopic images), as well as microstructural features such as toughness pockets.

 

Characteristics of fatigue fracture

(1) There is no obvious macroscopic plastic deformation during fracture, and there is no obvious precursor before fracture. It often occurs suddenly, causing damage or fracture of mechanical parts, which is very harmful.

(2) The stress causing fatigue fracture is very low, often lower than the stress load at the yield strength under static load.

(3) After fatigue failure, the three regions of crack initiation, propagation, and final fracture can usually be clearly observed at the fracture surface.

 

The cause of fatigue fracture of carbide tools

The service conditions of cemented carbide tools are generally harsh, often requiring cyclic loading, alternating temperature changes between hot and cold, and corrosive environments. Fatigue is a major cause of damage to cemented carbide workpieces.

Generally speaking, fatigue types include mechanical fatigue, thermal fatigue, corrosion fatigue, etc. In practical applications, several types of fatigue act together and promote each other. Currently, most of the reports on the properties of cemented carbides are related to static load, mainly including hardness, bending strength, fracture toughness, etc.

Fatigue fracture of carbide cutting tool

Cemented carbide tools are constantly subjected to alternating bending stresses, frequent shocks, and thermal fatigue caused by rapid cooling during idle periods during use, which inevitably leads to stick-slip and chipping. These are the various cracks that occur in the cutting area due to fatigue, which gradually expand under cyclic loading until failure.

How does the fatigue fracture of cemented carbide material occur? 3

Fatigue fracture of carbide mining tools

In mining and excavation, it is necessary to achieve this through the rotation, impact, and combination of the two effects of carbide tools. During frequent contact with rock, carbide tools produce impact fatigue, and at the same time generate a large amount of heat due to severe friction, with local temperatures reaching over 1000°C. Meanwhile, under the action of water cooling or air cooling, thermal fatigue effects occur. For mining conditions in medium and soft hardness rocks, due to the small impact load on the rock, the main cause of damage is the expansion of crack sources caused by thermal fatigue under the combined action of impact load and thermal cycle, which ultimately leads to instability and final fracture of the workpiece. The final damage characteristics of this tool are the presence of “snake skin” cracks caused by thermal fatigue. During hard rock mining, the drill teeth mainly bear a large impact load, so the main damage is caused by impact fatigue. Physical or chemical changes in the surface area induce crack nucleation, which then grows and destroys. The increase in temperature accelerates this physical or chemical change, thereby exacerbating the material damage.

How does the fatigue fracture of cemented carbide material occur? 4

As a coal mining tool, carbide pick is subjected to high reciprocal compressive stress, shear stress, and impact load, and is also affected by temperature changes, making its service conditions quite complex.The main causes of fracture in coal mining pick blades are the combined effects of surface cracking caused by brazing, thermal fatigue, and impact fatigue.

Fatigue fracture of carbide die

Cemented carbide molds have been subjected to dynamic loads such as drawing, extrusion, and impact during use, as well as to thermal cycles due to friction or high-temperature operations, and even to the corrosive effects of cooling fluids. For example, the YG alloy used in drawing steel wire molds is ultimately destroyed due to stress corrosion cracking caused by selective dissolution of the Co binder phase in the lubricating fluid, leading to formation of a fracture source.

fatigue fracture of cemented carbide roll

How does the fatigue fracture of cemented carbide material occur? 5

During the normal use of the roll (ring), the general damage begins with surface “cracks”. This kind of crack is usually caused by thermal fatigue cracks generated by the interaction of friction heat and cooling water generated during the use of the surface. As this network-like cracks extend, it gradually causes alloy peeling and even crushing of the roll. Research indicates that the actual damage analysis of wire and rod rolls shows that the fracture source mainly originates from the voids inside the material and the groove bottom or groove surface of the roll.

 

Methods for improving material fatigue limit or fatigue strength

It is generally difficult to change the service conditions of parts, and it is necessary to improve the design of parts as much as possible, such as starting with surface effects. As long as the structural materials and mechanical parts are prevented from surface stress concentration, dislocation slip accumulation, and plastic deformation, fatigue cracks are not easy to nucleate and expand, which will increase the fatigue limit or fatigue strength.

Measures to slow down stress concentration

Square or sharp-angled holes and slots should be avoided in the design.

For sudden changes in cross-sectional dimensions (such as the shoulder of a stepped shaft), use a transition fillet with a sufficiently large radius to reduce stress concentration.

When it is difficult to increase the radius of the transition fillet due to structural reasons, a thinning groove or relief groove can be cut on the part of the shaft with a larger diameter.

Strengthen the surface strength

Mechanical methods are used to strengthen the surface layer (such as rolling, shot blasting, etc.), which results in a pre-stressed layer on the surface of the component, reducing the surface tensile stress that is prone to causing cracks, thereby improving fatigue strength. Alternatively, thermal and chemical treatments such as high-frequency quenching, carburizing, nitriding, etc. can be used.

Use small gravel with a diameter of 0.1-1mm to impact the surface of the sample at high speed to remove sharp corners, burrs, and other areas prone to stress concentration, and compress the surface to a depth of 1/4-1/2 the diameter of the steel ball, causing residual stress on the surface of the part and inhibiting the propagation of fatigue cracks.

 

Bir cevap yaz?n

E-posta hesab?n?z yay?mlanmayacak. Gerekli alanlar * ile i?aretlenmi?lerdir

亚洲黄片免费观看高清-精品国产中文字幕av-60分钟三级全黄50岁-国产精品东北重口变态| 亚洲av无一区二区三区久久-色琪琪久久综合网天天-国产一区二区视频在线播放-大象焦伊人久久综合网| 开心五月激情五月综合-国产88精品久久久久久-乱人伦精品视频在线观看-秘社一区二区三区一午夜日本| 亚洲av男人的天堂久久精品-人妻中文字幕一区二区视频-国产男女乱淫真视频播放-国内人妻自拍交换在线视频| 四虎在线观看永久免费-久久精品熟女亚洲av香蕉-av国内精品久久久久影院三级-亚洲国产一区二区三区av| 精品视频人妻少妇一区二区三区-人妻中文字幕一二三区-日本老熟妇成熟老妇人-东京热国产精品二区三区| 国产精品久久中文字幕网-国产亚洲av无色肉丝网站-自拍偷拍亚洲精品偷一-日本久久一区二区三区| 亚洲天堂成人免费视频-青草精品在线观看视频-国产三级在线观看国产精品-黄色日本黄色欧美视频| 精品国产成人亚洲午夜福利-午夜福利一区二区91-亚洲中文字幕女优最新网址-亚洲av成人国产精品| 国产精品国产三级在线试看-亚洲男人天堂一区二区在线观看-风韵丰满熟妇啪啪区99杏-最近中文字幕日韩有码| 少妇特殊按摩高潮连连-国产成熟美女三级视频-亚洲男人天堂成人免费-国产粉嫩美女在线观看| 青草黄色成人中文视频-国产剧情av在线大学生-日韩av在线一卡二卡三卡-国产成人午夜福利影院| 亚洲精品成人久久av中文字幕-中文av毛片在线观看-一本之道加勒比在线视频-日韩av一区二区在线观看不卡| 欧洲激情综合啪啪五月-国产精选三级在线观看-七七久久成人影院网站-男人深夜福利在线观看| 精品人妻一区二区三区三区四区-亚洲中文字幕熟女一区二区-91久久精品国产91性色69-国产精品中文字幕中文字幕| 五月激情综合网俺也去-美欧日韩一区二区三区视频-午夜看片福利在线观看-色老板在线免费观看视频日麻批| 四只虎视频大全免费观看-日本黄色激情免费网站-免费岛国大片在线播放-国产午夜福利在现观看| 久久女婷五月综合色啪色老板-国内不卡的一区二区三区中文字幕-在线观看一区二区三区日韩-五月天丁香婷婷狠狠狠| 亚洲一级特黄大片做受-国产91喷潮在线观看-日本不卡一区二区三区四区-在线观看高清视频一区二区三区| 国产美女口爆吞精服务-亚洲无人区码一码二码三码-久久精品99国产精品最新-日本少妇激情在线视频| 国产四虎视频在线观看-日本一区二区三区暖暖视频免费-91人妻人人澡人人添人人爽-在线日本高清日本免费| 综合一综合二综合久久-亚洲一区二区三区视频免费观看-亚洲国产中文字幕一区二区-日韩人妻一区二区三区蜜桃视频| 密臀av免费在线观看-日韩欧美中文字幕美利坚-av黄色在线观看一区二区三区-日韩性做爰片免费视频看| 成人精品一区二区三区久久-中文字幕乱码亚洲无线三区-亚洲精品亚洲人成人网-中文字幕五月久久婷热| 亚洲欧美日韩另类第一页-亚洲欧美日本综合久久-亚洲一本之道高清在线观看-不卡在线一区二区三区视频| 国产精品99一区二区三区-伦理激情婷婷综合五月天-综合久久av一区二区三区-99精品国产在热久久| 国产午夜精品视频在线观看-亚洲欧洲日本元码高清-亚洲精品视频自拍成人-午夜福利欧美在线观看视频| 男女激情四射午夜福利视频网站-人成午夜免费毛片直接观看-日本女优在线观看一区二区-青草国内精品视频在线观看| 国产成人综合中文字幕-中文字幕午夜五月一二-在线视频精品一区二区三区-久久96精品国产亚洲av蜜臀| 超碰国产传媒在线观看-av在线免费观看蜜臀-亚洲欧美国产一区二区综合-人妻久久精品夜夜爽一区二区| 人日本中文字幕免费精品-日本口爆吞精在线视频-玖玖玖玖视频在线观看-国产精品内射在线播放| 久热在线视频精品99-国产欧美日韩久久午夜-在线观看亚洲精品91-黄色大片一区二区久久精品视频| 国产精品午夜福利免费在线-99热首页这里只有精品-国产一区二区三区精品观看-宅男午夜一区二区三区| 成人福利一区二区视频在线-亚洲婷婷综合久久一本伊一区-日本高清午夜一区二区三区-日韩欧美黄色激情视频| 超碰成人av免费观看-伊人色综合久久天天伊人婷-av天堂激情在线观看-国产精品自拍国产精品| 成a级人在线观看网站免费看-久久久精品国产亚洲av水蜜桃-亚洲第一狼人在线观看-黄色欧美精品一区二区三区| 邻居少妇毛多水多太爽了-男人天堂手机在线视频-国产精品国产三级国产专播-韩国女主播福利视频一区二区| 欧洲亚洲高清另类清纯-国产av一区二区三区av-亚洲精品一区二区三区午夜-国产夫妻自拍3p视频在线| 日韩av高清不卡一区二区-国产亚洲性色av大片久久香蕉-国产亚洲欧美韩国日本-国产精品国产三级国产普通话对白| 亚洲不卡av影院在线-久久精品伊人久久精品-亚洲国产日韩欧美三级-久久亚洲中文字幕精品二区| 熟女人妻中文字幕在线视频-91久久成人精品探花-国产精品黄色一区二区三区-99精品国产99久久久久97|