A mechanical seal is a device that relies on elastic components to pre-tighten the sealing faces of the static and rotating rings, and uses the pressure of the medium combined with the pressure of the elastic components to achieve axial balance, thus ensuring axial face sealing. Figure 1 shows a common type of mechanical seal structure. In the sealing area, the rotating ring and the stationary ring’s faces slide relative to each other. Due to the combined effects of heat, chemicals, physical forces, and mechanical factors, these contact surfaces are most prone to leakage or even damage. The operational condition of the sealing rings determines the performance and lifespan of the mechanical seal, and the performance of the sealing ring materials directly affects its operational condition. Therefore, understanding the performance requirements of sealing materials for mechanical seals and selecting appropriate sealing materials are crucial for ensuring the safe operation of mechanical seals.

 

Requirements for Seal Face Materials in Mechanical Seals

To ensure the proper operation of sealing rings in mechanical seal devices, they are typically configured as a pair consisting of a hard ring and a soft ring with different hardness levels, considering aspects such as wear reduction, corrosion resistance, and prevention of galling. During operation, the sealing rings may come into contact and generate friction when starting, stopping, or experiencing fluctuations in working conditions. Therefore, the material for the hard ring needs to have sufficient strength, rigidity, wear resistance, and thermal conductivity. Friction and fluid shear forces can elevate the temperature of the sealing rings, so the sealing material must exhibit good thermal conductivity, heat resistance, and thermal shock resistance. To ensure a long service life, the sealing ring must also have good corrosion resistance. Additionally, the hard ring should possess good formability and machinability, low density and permeability, and excellent self-lubricating properties. No single material can fully meet all these requirements, so typically, the main performance criteria for sealing materials are defined based on the operating environment, and suitable materials are selected accordingly.

mechanical seal ring

Application of WC-Ni carbide as Mechanical Seal Materials

To ensure the longevity and stable operation of mechanical seal materials, the sliding materials should have appropriate thermal compatibility and thermal conductivity, as well as suitable coefficients of thermal expansion, elastic modulus, and friction factors. WC-Ni carbides are known for their excellent performance in mechanical seals, making them suitable for applications in high-pressure, high-speed, high-temperature, corrosive environments, and media containing solid particles.

Application of WC-Ni carbide?in Mechanical Seal Face Materials 2

Characteristics of WC-Ni carbide

Since the introduction of carbides in the 1920s, cobalt has been regarded as the best binder phase and continues to play a significant role in the preparation of carbides. With the rapid advancement of science and technology, the applications of carbides have expanded, leading to a surge in demand. Due to the scarcity of cobalt resources, scientists worldwide have prioritized cobalt as a strategic material and have been researching ways to reduce or substitute cobalt in carbides. Nickel, being close to cobalt in the periodic table, with similar density, melting point, and atomic radius, can effectively wet and support the hard phase and has lower radioactivity compared to cobalt, making it a common substitute.

The characteristics of WC-Ni and WC-Co carbides during the sintering process are similar. However, due to the different strengthening effects of Ni and Co on the hard phase, WC-Ni may exhibit slightly lower performance in certain aspects compared to WC-Co carbides. By adding a small amount of metal elements to enhance the binder phase, using fine low-carbon WC particles, and employing vacuum sintering processes, WC-Ni carbides with lower porosity and a uniform, fine-grained structure can be achieved. Their hardness, bending strength, and tribological properties can meet or exceed those of WC-Co carbides, while their corrosion resistance is also significantly improved. Additionally, as Ni replaces the radioactive element Co, it provides good radiation protection when used under radioactive conditions. By carefully controlling the total carbon content and grain size of the alloy, and adding appropriate amounts of Mo and Cr, WC-Ni carbides can be produced with non-magnetic properties and excellent physical and mechanical performance, thereby mitigating the effects of special working conditions and environmental factors.

Application of WC-Ni carbide?in Mechanical Seal Face Materials 3

Physical and Mechanical Properties of WC-Ni carbide for Mechanical Seals

WC-Ni carbides are made by mixing WC and Ni powders in a specific ratio, adding a binder, and then pressing and sintering the mixture. With a melting point of approximately 2700°C, WC particles are primarily bonded together during the sintering process through the melting of Ni. At high temperatures, some WC dissolves into Ni, forming a WC-Ni eutectic with a lower melting point than Ni. Consequently, the sintering temperature varies with changes in Ni content and WC grain size. For composite materials, physical parameters such as elastic modulus, coefficient of thermal expansion, Poisson’s ratio, thermal diffusivity, and thermal conductivity can vary based on the proportion and distribution of each phase.

Application of WC-Ni carbide Materials in Mechanical Seals

Due to their exceptional toughness, rigidity, high hardness, good wear resistance, high bending strength, and high thermal conductivity, both WC-Ni and WC-Co carbides are notable. WC-Ni carbides offer superior corrosion resistance compared to WC-Co alloys and do not emit radiation under neutron exposure, making them suitable for use in mechanical seals operating under high pressure, high speed, high temperature, corrosive media, media containing solid particles, and radioactive environments. Currently, WC-Ni carbides have significant application value in vehicle transmission shaft seals, power shift transmissions, pumps in special operating conditions, and rotary seals for aircraft, as well as in the petrochemical industry and nuclear power seals.

Influence of Microstructure on the Properties of WC-Ni carbides

Application of WC-Ni carbide?in Mechanical Seal Face Materials 4

The unevenness in microstructure can adversely affect the strength of carbides. Minor variations in the binder phase content and distribution, WC grain size, carbon content, and any form of impurity contamination can lead to an uneven microstructure that negatively impacts the mechanical properties of WC-Ni carbides.

Influence of WC Grain Size on the Properties of WC-Ni carbides

WC-Ni carbides use Ni as the binder metal. During the sintering process, Ni melts at the sintering temperature and bonds the WC particles together into a solid mass. These alloys exhibit very high hardness, are difficult to machine, and possess excellent wear resistance. Variations in the processing methods can lead to significant differences in the alloy’s composition and properties, and the morphology of the WC grains can also affect the performance of WC-Ni carbides.

3.2Changes in WC Grain Morphology During Liquid Phase Sintering of WC-Ni carbides

The coarseness of WC grains can significantly affect the bending strength of carbides, while uneven distribution of Ni can lead to brittle fracture of the alloy. To improve the fracture toughness of the product, it is essential to strengthen the interface between WC and the binder phase or to enhance the strength of the binder phase. Therefore, controlling the sintering process and conditions will impact the mechanical properties of WC-Ni carbides.

During sintering, the shape of WC grains in the carbide?is also influenced by shape relaxation and the grain growth process. The higher the ratio of the average intercept length of the binder phase (the average length of each grain intersected by any testing line on a cross-section) to the WC grain size, the less impact it has on the shape of the WC grains, resulting in a more equiaxed grain morphology.

Application of WC-Ni carbide?in Mechanical Seal Face Materials 5

Effect of Binder on Temperature Residual Stress in WC-Ni carbides

When the content of the metallic binder Ni in WC-Ni alloy materials is relatively high, the compressive stress in fine WC grains is greater than that in coarse grains. This is because, with a constant WC content, the average free path of the binder in fine powder is shorter than in coarse powder. When the WC-Ni alloy contains less binder, the difference in the average free path of the binder is minimal, and the variation in residual stress with temperature is not significant. Therefore, if conditions allow, the Ni content in WC-Ni alloy sealing rings should be reduced to minimize the uneven distribution of residual stress due to temperature changes, thus reducing or even preventing thermal cracking in the sealing rings.

Current Research Status on the Application Performance of WC-Ni carbides

?Corrosion Resistance of WC-Ni Alloys

Compared to WC-Co carbides, WC-Ni carbides exhibit superior wear resistance. This is due to the binder in WC-Ni alloys having excellent corrosion resistance, with both passivation and electrochemical corrosion rates for WC-Ni carbides being significantly lower than those for WC-Co carbides. Under acidic conditions in practical production processes, WC alloys with Ni as the binder show better acid resistance than those with Co as the binder.

Table 2 compares the corrosion resistance of WC-Ni and WC-Co carbides. The results show that substituting Co with Ni significantly enhances the corrosion resistance of WC carbides. However, the corrosion resistance of a material is specific to its alloy composition, grain size, and the corrosive conditions (including temperature, concentration, time, and corrosion state). For example, the corrosion resistance of YWN8 in 68%-90% HNO? is not significantly different from, and even slightly lower than, that of YG6 alloy. This is primarily due to the poor resistance of metallic Ni to strong oxidizing acids like HNO?; as the concentration of HNO? and the Ni content in the alloy increase, its corrosion resistance decreases.

Table 2 Corosion resistance performance comparison between WC-Ni and WC-Co cemented carbides

Tribological Performance of WC-Ni Alloy Mechanical Seal Rings

WC-Ni carbide?sealing rings exhibit excellent wear resistance. This is because WC-Ni carbides possess strong oxidation resistance and corrosion resistance in fluid sealing media, which contributes to their superior wear resistance. The friction coefficient of WC-Ni carbides is related to the content, grain size, and distribution of the binder phase. A softer binder phase can lead to adhesion during friction. Additionally, the content and composition of the binder phase can affect the hardness of WC-Ni, thereby influencing the wear resistance of the WC-Ni carbide.

 

Wniosek

Mechanical seal materials are a crucial area of research in sealing technology. With the advancement of modern science and technology and the increasing demands of production and daily life, the requirements for sealing technology have become more stringent. However, research in this field in our country is still relatively behind. Strengthening interdisciplinary collaboration and continually improving experimental and theoretical research are key to overcoming the technological barriers in mechanical seals imposed by foreign countries.

Dodaj komentarz

Twój adres email nie zostanie opublikowany. Pola, których wype?nienie jest wymagane, s? oznaczone symbolem *

免费在线观看午夜视频-成人性生交大片免费网站-国产一区二区精品久久胖女人-亚州综合国产精品天码av| 免费亚洲毛片在线播放-国产精品国产三级国产专区不卡-亚洲欧美日韩狂野精品-白嫩丰满人妻荫蒂毛茸茸| 黄色av日韩在线观看-偷拍自拍在线免费视频-色偷偷偷亚洲综合网另类-国产成人免费综合视频| 中文在线字幕亚洲精品-91麻豆天美精东蜜桃专区-黄色av电影免费在线观看-国产三级四级在线播放| 久久精品亚洲精品毛片-国产精品白丝在线播放-日韩国产欧美综合第一页-亚洲三a免费观看网站| 日韩一卡二卡在线播放-亚洲国产精品懂色av-青青热久免费精品视频在-久久精品中文字幕一区二区三区| 国产精品爽爽va在线观看-亚洲av永久一区二区三区综合-成人av免费大片黄在线观看-一本一道久久a久久综合精品| 亚洲av乱码久久观看-亚洲爆码一区二区三区-91亚洲国产精品视频-黑丝美女被爆操流白浆| 午夜视频在线观看免费国产-国产精品91在线视频-欧美黄片在线免费播放-久久综合九色综合婷婷| 99久久免费精品老色-白色白色在线观看视频-91麻豆精品在线播放-日本人妻少妇中文字幕| 91老熟女老女人国产老太-av在线亚洲av男人的天堂-国产精品久久久区三区天天噜-能看不卡视频网站在线| 国产视色精品亚洲一区二区-激情艺术中心国产精品-国产农村一级特黄真人片-免费观看午夜视频在线| 91精品国产在热久久-亚洲欧美乱综合小说区-丰满少妇被粗大猛进人高清-99精品国产一区二区青青性色| 国产精品国产三级在线试看-亚洲男人天堂一区二区在线观看-风韵丰满熟妇啪啪区99杏-最近中文字幕日韩有码| 亚洲天堂久久中文字幕-高清国产一级片免费看-伊人狼人综合日日夜夜-手机看片高清国产日韩| 国产一级片内射在线视频-亚洲少妇无套内射激情-成人午夜性色福利视频-夜夜嗨视频无套实战丰满少妇| 成人在线自拍偷拍视频-国产剧情av中文字幕-久久国产劲爆内射日本-劲爆欧美中文字幕精品视频| 久久精品国产普通话对白-丰满人妻中文字幕一区二区-国产日本精品视频在线观看-香港免费毛片在线观看| 日韩久久久久久中文字幕-九九热视频精选在线播放-亚洲最大黄色成人av-亚洲最大av一区二区| 欧美高清视频在线高清观看-四虎最新在线播放视频-亚洲中文字幕永久在线全国-亚洲国产av成人精品成人| 中文一区二区三区免费毛片-99久久久69精品一区二区三区-精品国产一级二级三级在线-初撮五十路熟女柏木舞子| 国产色片地址网日本激情-国产自偷在线拍精品热不卡-国产精品自产拍蜜臀av在线-成人区人妻精品一区二区三区| 日韩av二区三区亚洲综合-日韩有码中文字幕国产-国产精品视频一二三四五区-青春草在线视频免费观看| 亚洲精品在线观看蜜臀-亚洲日本va中文字幕久久-欧美不雅视频午夜福利-日韩卡一卡二卡三卡四| 国产成人综合激情婷婷-亚洲国产综合在线观看不卡-色综网久久天天综合狼人-亚洲av高清在线不卡| 午夜精品福利激情视频-婷婷国产五月天网久久精品-国产av麻豆嫩草视频-av日本中文字幕在线| 欧美黄色在线观看免费-日本高清精品一卡二卡-日本综合精品一区二区在线-国产精品伦人一久二久三久| 国产精品欧美日韩视频二区-少妇人妻系列中文在线-精品人妻一区二区三区四区不卡-少妇被无套内谢免费视频| 亚洲国产国语对白在线视频-中文字幕中文字字幕码一区二区-毛片av在线免费观看-免费在线观看av毛片| 亚洲精品色国语对白在线-黄片毛片av在线免费观看-久久精品有码av天堂-日韩一区二区三区高清视频| 午夜性福福利视频一区二区三区-午夜福利在线看片在线-欧洲内射免费人文艺术-亚洲天堂成人av在线| 亚洲永久精品在线观看-成人av在线观看免费-蜜臀av免费一区二区三区-成人av在线久色播放| 中文字幕日韩精品人妻久久久-午夜福利激情视频在线观看-蜜桃黄网站视频在线观看-国产丰满熟女夜夜嗨av| 中文字幕一区二区三区日韩精品-久久老熟女一区二区三区福利-久久精品国产自产对白一区-午夜欧美牲交激情网站| 18禁成人一区二区三区av-亚洲热热日韩精品中文字幕-亚洲中文字幕视频第一二区-亚洲国产日韩精品在线| 国产女主播在线播放福利-日韩中文字幕综合第二页-av男人的天堂免费观看-国产乱码免费一区二区三区不卡| 国产精品乱码一区二区三区视频-国产自拍精品在线一区二区-五月综合丁香婷婷久久-在线国产精品一区二区三区| 国产精品女同一区二区久久夜-日本精品女人一区二区三区-亚洲成人久久久久久-激情五月婷婷综合激情| 欧美亚洲国产另类在线-九九热精品在线免费视频-日本高清有码在线一区-青草第一视频在线观看| 免费手机在线观看bbb视频-国产欧美亚洲精品第1页青草-国产黄a三级三18级三级看三级-宅男视频在线观看一区二区三区| 亚洲av色福利天堂在线观看-人妻少妇午夜福利视频-男人的天堂av在线视频-国内揄拍国产精品人妻一区二区|